Title: Estudo do efeito de memória de forma de fios ortodônticos da liga Ni-Ti nas condições comercial e após tratamentos térmicos
Author(s): Geroldo, Augusto César de Brito
Advisor: Santos, Carlos Alexandre dos
Publisher: Pontifícia Universidade Católica do Rio Grande do Sul
Graduate Program: Programa de Pós-Graduação em Engenharia e Tecnologia de Materiais
Issue Date: 2009
Keywords: ENGENHARIA DE MATERIAIS
RESISTÊNCIA DOS MATERIAIS
LIGAS ODONTOLÓGICAS
Abstract: A liga de Ni-45%Ti em peso, conhecida desde a década de 70 e denominada NITINOL®, apresenta excelentes características de resistência à corrosão, resistência a fadiga, biocompatibilidade e elevadas propriedades mecânicas. As ligas Ni-Ti apresentam recuperação de forma (E. M. F – Efeito de Memória de Forma) de até 8%, com temperatura de recuperação variando de -50°C a +110°C, dependendo da composição química da liga e da microestrutura, tendo como principais aplicações: áreas aeroespacial, naval, nuclear, automobilística, utilidades domésticas, robótica, com destaque nas áreas médica e odontológica. O objetivo do presente trabalho é o estudo da liga Ni-Ti em relação ao E. M. F e comparação de propriedades mecânicas e estruturas por meio de análises metalográficas (microscopia óptica e eletrônica), ensaios de microdureza Vickers, difração de raios X e fluorescência de raios X, nas condições: fios comerciais e após tratamentos térmicos de normalização em diferentes temperaturas (TTx): 300°C, 500°C e 700°C. Os resultados foram correlacionados com a microestrutura resultante e as condições de tratamento térmico. Concluiu-se que de acordo com os objetivos estabelecidos e as técnicas de caracterização e ensaios utilizados, a amostra com melhor rendimento foi à tratada termicamente a 500°C.
The Ni-45wt%Ti alloy, called as NITINOL®, presents excellent characteristics of corrosion resistance, fatigue resistance, biocompatibility and improved mechanical properties. The properties of Shape Memory Effect Alloys (SMAs) are dependents of the thermomechanical treatments after solidification. The Ni-Ti alloys present recovery of form up to 8%, with recovery temperature varying of -50°C to +110°C, depending on the chemical composition and the microstructure. The main applications of these alloys are: aerospace, naval, nuclear, automobile, utilities, robotics, and medical and odontologic areas. The objective of this work is the study of the SMA in the Ni-Ti alloy and the comparison of structures mechanical and properties by metallographic analyses (optic and electronic microscopy), microhardness Vickers, X rays diffraction and X rays fluorescence in the conditions: commercial wires and after thermal treatments of annealing in different temperatures (TTx): 300°C, 500°C and 700°C. After removed of the furnace, the samples were analysed in relation to the EMF in identical conditions of deformation and recovery temperature. The results were correlated with the resultant microstructure and the conditions of heat treatment. It was concluded that in accordance with the objectives established and the techniques used for characterization and testing, the sample with the best performance was heat treated at 500°C .
URI: http://hdl.handle.net/10923/3277
Appears in Collections:Dissertação e Tese

Files in This Item:
File Description SizeFormat 
000412506-Texto+Completo-0.pdfTexto Completo6,01 MBAdobe PDFOpen
View


All Items in PUCRS Repository are protected by copyright, with all rights reserved, and are licensed under a Creative Commons Attribution-NonCommercial 4.0 International License. Read more.