dc.description.abstractA liga de Ni-45%Ti em peso, conhecida desde a década de 70 e denominada NITINOL®, apresenta excelentes características de resistência à corrosão, resistência a fadiga, biocompatibilidade e elevadas propriedades mecânicas. As ligas Ni-Ti apresentam recuperação de forma (E. M. F – Efeito de Memória de Forma) de até 8%, com temperatura de recuperação variando de -50°C a +110°C, dependendo da composição química da liga e da microestrutura, tendo como principais aplicações: áreas aeroespacial, naval, nuclear, automobilística, utilidades domésticas, robótica, com destaque nas áreas médica e odontológica. O objetivo do presente trabalho é o estudo da liga Ni-Ti em relação ao E. M. F e comparação de propriedades mecânicas e estruturas por meio de análises metalográficas (microscopia óptica e eletrônica), ensaios de microdureza Vickers, difração de raios X e fluorescência de raios X, nas condições: fios comerciais e após tratamentos térmicos de normalização em diferentes temperaturas (TTx): 300°C, 500°C e 700°C. Os resultados foram correlacionados com a microestrutura resultante e as condições de tratamento térmico. Concluiu-se que de acordo com os objetivos estabelecidos e as técnicas de caracterização e ensaios utilizados, a amostra com melhor rendimento foi à tratada termicamente a 500°C.pt_BR
dc.description.abstractThe Ni-45wt%Ti alloy, called as NITINOL®, presents excellent characteristics of corrosion resistance, fatigue resistance, biocompatibility and improved mechanical properties. The properties of Shape Memory Effect Alloys (SMAs) are dependents of the thermomechanical treatments after solidification. The Ni-Ti alloys present recovery of form up to 8%, with recovery temperature varying of -50°C to +110°C, depending on the chemical composition and the microstructure. The main applications of these alloys are: aerospace, naval, nuclear, automobile, utilities, robotics, and medical and odontologic areas. The objective of this work is the study of the SMA in the Ni-Ti alloy and the comparison of structures mechanical and properties by metallographic analyses (optic and electronic microscopy), microhardness Vickers, X rays diffraction and X rays fluorescence in the conditions: commercial wires and after thermal treatments of annealing in different temperatures (TTx): 300°C, 500°C and 700°C. After removed of the furnace, the samples were analysed in relation to the EMF in identical conditions of deformation and recovery temperature. The results were correlated with the resultant microstructure and the conditions of heat treatment. It was concluded that in accordance with the objectives established and the techniques used for characterization and testing, the sample with the best performance was heat treated at 500°C .en_US
dc.language.isoPortuguêspt_BR
dc.publisherPontifícia Universidade Católica do Rio Grande do Sulpt_BR
dc.subjectENGENHARIA DE MATERIAISpt_BR
dc.subjectRESISTÊNCIA DOS MATERIAISpt_BR
dc.subjectLIGAS ODONTOLÓGICASpt_BR
dc.titleEstudo do efeito de memória de forma de fios ortodônticos da liga Ni-Ti nas condições comercial e após tratamentos térmicospt_BR
dc.typemasterThesispt_BR
dc.degree.grantorPontifícia Universidade Católica do Rio Grande do Sulpt_BR
dc.degree.departmentFaculdade de Engenhariapt_BR
dc.degree.programPrograma de Pós-Graduação em Engenharia e Tecnologia de Materiaispt_BR
dc.degree.levelMestradopt_BR
dc.degree.date2009pt_BR
dc.publisher.placePorto Alegrept_BR
Aparece en las colecciones:Dissertação e Tese

Ficheros en este ítem:
Fichero Descripción TamañoFormato 
000412506-Texto+Completo-0.pdfTexto Completo6,01 MBAdobe PDFAbrir
Ver


Todos los ítems en el Repositorio de la PUCRS están protegidos por derechos de autor, con todos los derechos reservados, y están bajo una licencia de Creative Commons Reconocimiento-NoComercial 4.0 Internacional. Sepa más.