dc.description.abstractDispersões aquosas de poliuretano (DPUs) têm sido utilizadas na área de revestimentos, adesivos, selantes, entre outras. Na preparação desses sistemas existem diversas variáveis, tais como: a natureza dos reagentes de partida, a razão NCO/OH, a concentração de grupos iônicos, os graus de neutralização e extensão de cadeia e o tipo de processo de síntese que podem modificar características como massa molar (MM), viscosidade ( ) e tamanho de partícula. Este trabalho apresenta a síntese e a caracterização de DPUs utilizando-se dois diisocianatos: tetrametilxileno diisocianato (TMXDI) e isoforona diisocianato (IPDI) além de diferentes polióis. As DPUs foram sintetizadas pelo processo do pré-polímero e da acetona e caracterizadas por espectroscopia vibracional no infravermelho (IV), cromatografia de permeação em gel (GPC), tamanho de partícula e viscosidade Brookfield. O espectro de infravermelho deste material apresentou uma banda intensa em torno de 1730 cm-1 e duas bandas, de intensidade variável, em torno de 1246 cm-1 e 1180 cm-1 características do grupo uretano (NH-COO). O filme polimérico das DPUs sintetizadas possuem massa molar ponderal média em torno de 20000–100000 g/mol. A viscosidade obtida das DPUs possui valores entre 8–100000 mPa. s enquanto o tamanho de partícula médio está entre 61–430 nm.pt_BR
dc.description.abstractAqueous polyurethane dispersions (PUDs) have been used in the area of coatings, adhesives, sealants, among others. In the preparation these systems there are several variables, such as: the nature of raw materials, the NCO/OH rate, the ionic groups contents, the degrees of neutralization and chain extension and the type of process that can change features such as molar mass (MM), viscosity ( ) and particle size. This work presents the synthesis and characterization of PUDs using two diisocyanates: tetramethylxylene diisocyanate (TMXDI) and isophorone diisocyanate (IPDI) besides different polyols. The PUDs were synthesized through the processes of pre-polymer and of acetone and were characterized by infrared spectroscopy (IR), by gel permeation chromatography (GPC), by particle size and Brookfield viscosity. The infrared spectrum of this material presented an intense band around 1730 cm-1 and two bands of variable intensity, around 1246 cm-1 and 1180 cm-1 characteristics of the urethane group (NH-COO). The films of PUDs synthesized present average molecular weight around 20000–100000 g/mol. The viscosity of PUDs has value around 8–100000 mPa. s while the average particle size is at 61–430 nm.en_US
dc.language.isoPortuguêspt_BR
dc.publisherPontifícia Universidade Católica do Rio Grande do Sulpt_BR
dc.subjectENGENHARIA DE MATERIAISpt_BR
dc.subjectENGENHARIA QUÍMICApt_BR
dc.subjectPOLIURETANOSpt_BR
dc.subjectDISPERSÃO AQUOSApt_BR
dc.titleSíntese e caracterização de dispersões aquosas de poliuretanopt_BR
dc.typemasterThesispt_BR
dc.degree.grantorPontifícia Universidade Católica do Rio Grande do Sulpt_BR
dc.degree.departmentFaculdade de Engenhariapt_BR
dc.degree.programPrograma de Pós-Graduação em Engenharia e Tecnologia de Materiaispt_BR
dc.degree.levelMestradopt_BR
dc.degree.date2008pt_BR
dc.publisher.placePorto Alegrept_BR
Aparece nas Coleções:Dissertação e Tese

Arquivos neste item:
Arquivo Descrição TamanhoFormato 
000401347-Texto+Completo-0.pdfTexto Completo3,52 MBAdobe PDFAbrir
Exibir


Todos os itens no Repositório da PUCRS estão protegidos por copyright, com todos os direitos reservados, e estão licenciados com uma Licença Creative Commons - Atribuição-NãoComercial 4.0 Internacional. Saiba mais.