dc.contributor.advisorLigabue, Rosane Angélicaen_US
dc.contributor.authorCabral, Emanuelli Lourençoen_US
dc.date.accessioned2013-08-07T18:55:00Z-
dc.date.available2013-08-07T18:55:00Z-
dc.date.issued2012pt_BR
dc.identifier.urihttp://hdl.handle.net/10923/3365-
dc.description.abstractA procura por materiais que possam substituir ou restaurar tecidos danificados deve-se à busca por melhor qualidade de vida da população. Levando em consideração que doenças cardiovasculares são as principais causas de mortes no Brasil (Banco de Saúde, 2010), necessita-se de dispositivos que possuam eficácia na regeneração cardíaca, abordando questões de segurança à longo prazo e promovendo a cicatrização de vasos vasculares (PR Newswire, 2010). Neste sentido, o presente trabalho desenvolveu a síntese de poliuretanos bioestáveis a partir da reação de policaprolactona diol (PCL) com diferentes diisocianatos (HDI e H12MDI), caracterizando-os por meio de análise morfológica (MEV), térmica (TGA e DSC), mecânica (DMA) e estrutural (IV), como também, avaliando sua citotoxicidade in vitro, através de testes para a avaliação da viabilidade celular (teste VN e MTT) e proliferação celular (teste Azul de Tripan) utilizando células fibroblásticas NIH-3T3, comparando-os com materiais comerciais, Dacron e PTFE. Os resultados obtidos mostraram que os poliuretanos sintetizados apresentaram massa molar ponderal média (Mw) variando entre 30000 e 263000 g/mol, bem como, uma plasticidade dependente do poliol utilizado. O comportamento mecânico destes poliuretanos mostrou-se semelhante ou superior aos materiais comerciais, Dacron e PTFE. Os testes de bioestabilidade mostraram que houve perda de massa abaixo de 20% dos materiais expostos à degradação hidrolítica no periodo de 270 dias e abaixo de 5% na degradação enzimática no periodo de 30 dias. A viabilidade celular dos poliuretanos mostrou-se superior a 80%, consideradas não citotóxicas. Os poliuretanos avaliados neste estudo apresentaram resultados favoráveis para seu uso como biomaterial em possíveis aplicações cardiológicas.pt_BR
dc.description.abstractThe search for materials that can replace or restore damaged tissues is due to the search for better life quality of the population. Considering that cardiovascular diseases are the main causes of death in Brazil (Banco de Saúde, 2010), needs some devices that have efficacy in cardiac regeneration, addressing about issues of long-term safety and promoting the healing of vascular vessels (PR Newswire, 2010). In this sense, this paper developed the synthesis of biostable polyurethanes from the reaction of polycaprolactone diol (PCL) with different diisocyanates (HDI and H12MDI), characterizing them by morphological analysis (MEV), thermal (TGA and DSC), mechanical (DMA) and structural (IV), but also evaluating their in vitro cytotoxicity, by testing for the evaluation of cell viability (MTT and VN test) and cell proliferation (Trypan Blue test) using NIH-3T3 fibroblast cells, comparing them with commercial materials, Dacron and PTFE. The obtained results showed that the synthesized polyurethanes had average molar weight (Mw) ranging between 30000 and 263000 g/mol, as well as a plasticity depended of polyol used. The mechanical behavior of polyurethanes showed similar or greater than the commercial material, Dacron and PTFE. The biostability tests showed that there was mass loss below 20% of the materials exposed to hydrolytic degradation in the period of 270 days and below 5% in the enzymatic degradation in the period of 30 days. The cell viability of polyurethanes was superior to 80%, considered non-cytotoxic. Polyurethanes in this study showed favorable results for its possible use as biomaterial in cardiac applications.en_US
dc.language.isoPortuguêspt_BR
dc.publisherPontifícia Universidade Católica do Rio Grande do Sulpt_BR
dc.subjectENGENHARIA DE MATERIAISpt_BR
dc.subjectBIOPOLÍMEROSpt_BR
dc.subjectPOLIURETANOSpt_BR
dc.subjectMATERIAIS - TESTESpt_BR
dc.titleSíntese e caracterização de poliuretanos bioestáveis com potencial aplicação na área cardiovascularpt_BR
dc.typemasterThesispt_BR
dc.degree.grantorPontifícia Universidade Católica do Rio Grande do Sulpt_BR
dc.degree.departmentFaculdade de Engenhariapt_BR
dc.degree.programPrograma de Pós-Graduação em Engenharia e Tecnologia de Materiaispt_BR
dc.degree.levelMestradopt_BR
dc.degree.date2012pt_BR
dc.publisher.placePorto Alegrept_BR
Aparece en las colecciones:Dissertação e Tese

Ficheros en este ítem:
Fichero Descripción TamañoFormato 
000436434-Texto+Completo-0.pdfTexto Completo2,27 MBAdobe PDFAbrir
Ver


Todos los ítems en el Repositorio de la PUCRS están protegidos por derechos de autor, con todos los derechos reservados, y están bajo una licencia de Creative Commons Reconocimiento-NoComercial 4.0 Internacional. Sepa más.