Title: Avaliação da influência do eugenol na infiltração marginal em restaurações de resina composta em dentes decíduos
Evaluation of the influence of eugenol in dental leakage in composite resins restorations in deciduous teeth
Author(s): Braga, Gabriela Figueiredo
Stona, Priscila
Fritscher, Angélica Maria Genehr
Weber, João Batista Blessmann
Publisher: Universidade Estadual da Paraíba
Issue Date: 2011
Volume: 11
Issue: 3
First page: 371
Last page: 375
Keywords: CIMENTO DE ÓXIDO DE ZINCO E EUGENOL
RESINAS COMPOSTAS
INFILTRAÇÃO DENTÁRIA
ODONTOLOGIA
CIMENTAÇÃO (ODONTOLOGIA)
Abstract: Objetivo: Avaliar a infiltração marginal em restaurações de resina composta, realizadas sobre forramento com óxido de zinco e eugenol em molares decíduos. Método: Foram utilizados 24 molares decíduos divididos em três grupos (n=8/grupo), de acordo com o tempo decorrido até a realização da restauração de resina. G1= imediatamente após inserção do IRM; G2= após 48h e G3= após 28 dias. Uma cavidade oclusal foi realizada em cada dente com ponta montada diamantada 3018 HL. Depois de restaurados, os dentes foram cobertos por uma camada de esmalte e cera, deixando-se livre uma região de 1 mm ao redor da restauração. Os dentes foram, então, imersos no corante rodamina a 0,5% durante 24h. As amostras foram cortadas em máquina de corte (Labcut 1010), avaliadas em Estéreo Microscópio e classificadas por níveis de infiltração de 0 a 3. Os resultados foram submetidos aos teste Kruskall-Wallis e Qui-Quadrado, com nível de significância de 5%. Resultados: Constatou-se significativa associação entre infiltração e período decorrente até a realização da restauração. No período imediato houve menor grau de infiltração enquanto no período de 28 dias houve maior grau de infiltração (p=0,02). Conclusão: É importante que não haja muito tempo entre restauração provisória com IRM e restauração definitiva com resina composta a fim de diminuir a infiltração marginal.
Objective: to evaluate dental leakage in composite resin restorations carried through on the lining with zinc oxide and eugenol in molar deciduous. Methods: For the study, had been used 24 deciduous molars, which had been divided in three groups, in accordance with the moment where the resin restoration was carried through: G1= immediately after de insertion of the IRM, G2= after 48 hours and G3= after 28 days. A occlusal socket was carried through, in all the teeth, with a drill 3018 HL (KG Sorensen). After restored, the teeth had been covered enamel layer and wax, leaving itself around exempts a region of 1,, of the restoration. The teeth had been, then, immersed in rodamina dye 0.5% during 24 hours. After it was removed the enamel and the wax, and the teeth had been washed, dried and cut with a machine of precision cut (Labcut 1010). The specimens had been evaluated in a Stereo Microscope (Olympus SZH 10) and classified by levels of infiltration of 0 the 3. Results: Through the analysis statistics, a significant association was evidenced enters the presence of infiltration and the period where the restoration was carried through. It was observed that in the immediate period dental leakage had a minor and in the period of 28 days a bigger infiltration (p=0.02). Conclusion: It is important that there is not much time between temporary restoration with IRM and final restoration with composite resin to decrease microleakage.
URI: http://hdl.handle.net/10923/951
DOI: 10.4034/PBOCI.2011.113.10
ISSN: 1519-0501
Appears in Collections:Artigo de Periódico

Files in This Item:
File Description SizeFormat 
IRM Resina.pdfTexto Completo410,26 kBAdobe PDFOpen
View


All Items in PUCRS Repository are protected by copyright, with all rights reserved, and are licensed under a Creative Commons Attribution-NonCommercial 4.0 International License. Read more.