Campo DC | Valor | Idioma |
dc.contributor.advisor | Moehlecke, Adriano | en_US |
dc.contributor.author | Marcolino, Juliane Bernardes | en_US |
dc.date.accessioned | 2013-08-07T18:54:09Z | - |
dc.date.available | 2013-08-07T18:54:09Z | - |
dc.date.issued | 2011 | pt_BR |
dc.identifier.uri | http://hdl.handle.net/10923/3265 | - |
dc.description.abstract | A energia solar fotovoltaica baseada na conversão direta da energia solar em elétrica pode ser uma alternativa para a diversificação da matriz energética. O objetivo deste trabalho está centrado no desenvolvimento e na análise da deposição de pasta de Al por serigrafia e queima/difusão em forno de esteira para a formação de campo retrodifusor em lâminas de Si monocristalino. A difusão de Al foi implementada em dois diferentes processos. Foi realizada a difusão/queima da pasta Al e queima da pasta de Ag em passos independentes e, queima/difusão das pastas em passo simultâneo. Com o primeiro processo produziram-se células com eficiência média (ηmédia) de 11,5 % e máxima de 12,0 %, mas com problemas de formação de aglomerados de Al na superfície posterior. Com o segundo processo, os melhores resultados foram para temperatura de queima/difusão de 860 °C e velocidade de esteira (VE) de 150 cm/min e para temperatura de 890 °C e VE de 180 cm/min. Para o primeiro par de parâmetros, a ηmédia foi de 12,4 % e a máxima de 12,8 %. Para o segundo, o valor da ηmédia foi de 12,5 % e o máximo de 12,6 %. Considerando a temperatura de 900 °C e VE de 190 cm/min, a ηmédia foi de 12,4 %. Observou-se que o comprimento de difusão dos portadores minoritários foi menor que a espessura das lâminas de silício utilizadas neste trabalho. As tensões de circuito aberto ficaram da ordem de 30 mV menor do que células solares similares fabricadas no NT-Solar que usaram Al de alta pureza depositado por evaporação em alto vácuo, indicando que os processos realizados produzem um BSF de baixa qualidade. | pt_BR |
dc.description.abstract | Photovoltaics is based on the direct conversion of solar energy into electricity and is a promising alternative to diversify the world’s energy matrix. This work aims to develop and analyse the deposition of Al paste by screen printing and firing/diffusion in a belt furnace to produce a BSF region in monocrystalline Si wafers. The diffusion of Al into the substrate was implemented by two different processes. In the first process the diffusion/firing of the Al paste and the firing of the Ag paste was carried out in independent steps. In this case, solar cells with an average efficiency (ηaverage) of 11. 5 % and a maximum of 12. 0 % were produced, but with the formation Al clusters in the back surface of the devices. In the second process firing/diffusion of such pastes was done on the same step. In this case, the best results were obtained for a firing/diffusion temperature of 860 °C and belt furnace speed (VE) of 150 cm/min and also for 890 °C and 180 cm/min. For the former parameters, ηaverage was 12. 4 % and the maximum was 12. 8 %. For the later, ηaverage was 12. 5 % and the maximum was 12. 6 %. Considering a temperature of 900 °C and VE of 190 cm/min, ηaverage was 12. 4 %. It was observed that minority carriers diffusion lengths were smaller than the thickness of silicon wafers. Open circuit voltages were 30 mV lower than that from similar cells fabricated at NT-Solar by using high purity Al deposited by e-beam evaporation indicating that the developed process produced low quality BSF. | en_US |
dc.language.iso | Português | pt_BR |
dc.publisher | Pontifícia Universidade Católica do Rio Grande do Sul | pt_BR |
dc.subject | ENGENHARIA DE MATERIAIS | pt_BR |
dc.subject | CÉLULAS SOLARES | pt_BR |
dc.subject | DIFUSÃO | pt_BR |
dc.subject | ALUMÍNIO | pt_BR |
dc.title | Desenvolvimento de células solares com campo retrodifusor formado por pasta de alumínio e difusão em forno de esteira | pt_BR |
dc.type | masterThesis | pt_BR |
dc.degree.grantor | Pontifícia Universidade Católica do Rio Grande do Sul | pt_BR |
dc.degree.department | Faculdade de Engenharia | pt_BR |
dc.degree.program | Programa de Pós-Graduação em Engenharia e Tecnologia de Materiais | pt_BR |
dc.degree.level | Mestrado | pt_BR |
dc.degree.date | 2011 | pt_BR |
dc.publisher.place | Porto Alegre | pt_BR |
Aparece en las colecciones: | Dissertação e Tese
|