| Abstract: | Aims: to evaluate the bond strength of fibre-posts luted with two kind of resin cements to dentin of the root canal treated or not with Nd:YAG laser associated to phosphoric acid. Materials and methods: Sixty one-root teeth with similar morphology and length were submitted to the endodontic treatment with manual instrumentation. After, it were divided into six groups according to the luting protocol of the fibre post (n=10): G1 –RelyX Unicem; G2 – Nd:YAG laser + self-etching luting cement RelyX Unicem; G3 – 37% phosphoric acid gel (AG37%) + RelyX ARC; G4 – Nd:YAG laser + AG37% + RelyX ARC; G5 – etching with the Experimental Solution (ES): Patent number BRPI0903355-6) + RelyX ARC; e G6 – Nd:YAG laser + SS solution + RelyX ARC. The Nd:YAG laser were irradiated with the following protocol: 1064 nm, 60 mJ, 15 Hz and 47. 77 mJ/cm2, 1 min. Afterwards, the teeth with the luted fibre posts were stored in distilled water at 37ºC for 1 week. Next, the roots were sectioned in thirds – cervical, medial and apical – being the slices submitted to the push-out bond strength test. Results: the SS solution group associated to RelyX ARC presented together with the Nd:YAG laser associated to the RelyX Unicem the higher bond strength considering all thirds. Notwithstanding, the phosphoric acid gel associated to the RelyX ARC presented the lower bond strength together with the Relyx Unicem control group. Conclusion: The use of the ES solution increased significantly the bond strength of the RelyX Arc to dentin of the root canal.
Objetivos: Avaliar a resistência de união de pinos de fibra de vidro cimentados à dentina radicular tratada com laser de Nd:YAG, ácido fosfórico gel a 37% ou com uma solução experimental (PATENTE solicitada ao INPI nº PI0903355-6), utilizando dois tipos de cimentos resinosos. Materiais e métodos: Sessenta dentes unirradiculares com morfologia e comprimentos semelhantes foram submetidos ao tratamento endodôntico tradicional ou com laser de Nd:YAG, com instrumentação manual. Após, os dentes foram divididos em seis grupos de acordo com o protocolo de cimentação do pino de fibra de vidro (n=10): G1 –RelyX Unicem; G2 –laser Nd:YAG + RelyX Unicem; G3 –ácido fosfórico gel a 37% (AG37%) + RelyX ARC; G4 –laser Nd:YAG + AG37% + RelyX ARC; G5 – condicionamento com solução experimental (PATENTE solicitada ao INPI nº PI0903355- 6) + RelyX ARC; e G6 – laser Nd:YAG + solução experimental (PATENTE solicitada ao INPI nº PI0903355-6) + RelyX ARC. O laser de Nd:YAG foi irradiado com o seguinte protocolo: 1064 nm, 60 mJ, 15 Hz, 47,77 mJ/cm2 durante 1 min. Os dentes com os pinos cimentados foram armazenados em água destilada a 37ºC por 7 dias. Após esse período, as raízes foram seccionadas em terços cervical, médio e apical, sendo as fatias submetidas ao ensaio de resistência de união por push-out. Ainda, seis dentes foram submetidos aos tratamentos de superfície e levados à microscopia eletrônica de varredura e análise EDS. Resultados: o grupo da solução experimental (PATENTE solicitada ao INPI nº PI0903355- 6) associada ao cimento resinoso RelyX ARC apresentou juntamente com o grupo do laser 4 de Nd:YAG associado ao cimento RelyX Unicem a maior resistência de união considerando todos os terços radiculares. Por sua vez, o ácido fosfórico gel associado ao cimento RelyX ARC apresentou a menor resistência de união juntamente com o grupo do RelyX Unicem. Conclusão: O uso da solução experimental (PATENTE solicitada ao INPI nº PI0903355-6) aumentou significativamente a resistência de união do cimento resinoso RelyX ARC à superfície dentinária do conduto radicular, assim como a irradiação por laser, de uma maneira geral, também aumentou a resistência de união particularmente nos grupos G2 e G4. |
