dc.description.abstractO trabalho de pesquisa está relacionado com a preparação de compósitos de polietileno (PE) contendo carga condutiva baseadas na polianilina (PAni) e grafite. Nanofibras de PAni foram sintetizadas através do método da mistura rápida. Carga híbrida (PAni/NLG) foi sintetizada por meio da polimerização da anilina na presença de nanolâminas de grafite (NLG). Compósitos foram preparados utilizando-se diferentes metodologias: mistura por fusão e polimerização in situ. Na preparação de compósitos poliméricos de polietileno (PE)/PAni, PE/NLG e PE/PAni/NLG, por meio da polimerização in situ, foi utilizado sistema catalítico Cp2ZrCl2/MAO. As cargas condutivas assim como os compósitos produzidos foram caracterizados por MEV (Microscopia Eletrônica de varredura), TGA (Análise Termogravimétrica), DSC (Calorimetria Diferencial de Varredura) e propriedades elétricas (Sonda de Duas Pontas). A interação entre a PAni e o sistema catalítico Cp2ZrCl2/MAO foi investigada através da Técnica da Voltametria Cíclica e de Pulso Diferencial. A mistura rápida, metodologia de síntese de nanofibras mostrou-se eficiente, pois foram preparadas nanofibras com diâmetro de aproximadamente 50-80 nm e com rendimento de reação de 23%. A partir dos resultados constatou-se que a polimerizaçao in situ foi a metodologia mais adequada para produzir compósitos poliméricos na presença de PAni, visto que os compósitos apresentaram boa dispersão da carga induzindo à formação da rede condutiva. A presença de grafite no material híbrido melhora a condutividade elétrica dos compósitos e a qualidade das nanofibras é afetada positivamente. A metodologia da mistura por fusão não foi eficiente para dispersar as nanofibras de Pani na matriz de PE.pt_BR
dc.description.abstractThe research work is related to the preparation of polymer composites based on polyaniline (PAni) and graphite. Polyaniline nanofibers were synthesized by the method of rapid mixing. Hybrid load (PAni/NLG) was synthesized by polymerizing aniline in the presence of graphite nanosheets (NLG). Polymer composites were prepared using differents methodologies: melt blending and in situ polymerization. In preparing polymer composites of polyethylene (PE)/PAni, PE/NLG and PE/PAni/NLG by in situ polymerization, the catalyst system was used Cp2ZrCl2/MAO. Polymeric composites by melt blending with the melt PE and conductive load were prepared in the melting chamber. The conductive loads as well as those produced composites were characterized by Scanning Electron Microscopy (SEM), TGA (Thermogravimetric Analysis), DSC (Differential Scanning Calorimetry) and electrical properties (Probe Two Tips). Rapid mixing, nanofiber synthesis methodology was efficient, as were prepared nanofibers with a diameter of approximately 50-80 nm and with yield of the synthesis reaction of 23%. From the results it was found that the in situ polymerization was the most suitable method to produce polymeric composites in the presence of polyaniline, as the composite exhibited good load dispersion inducing the formation of the conductive network. The presence of graphite in hybrid material improves electrical conductivity of composites and the quality of nanofibers is affected positively. The methodology of the mixture by melting was not efficient to disperse the nanofiber Pani in PE matrix.en_US
dc.language.isoPortuguêspt_BR
dc.publisherPontifícia Universidade Católica do Rio Grande do Sulpt_BR
dc.rightsopenAccessen_US
dc.subjectENGENHARIA DE MATERIAISpt_BR
dc.subjectQUÍMICA INDUSTRIALpt_BR
dc.subjectPROCESSOS QUÍMICOS - SÍNTESEpt_BR
dc.subjectPOLIMERIZAÇÃOpt_BR
dc.subjectPOLÍMEROSpt_BR
dc.subjectNANOCOMPÓSITOSpt_BR
dc.titleSíntese de compósitos baseados em polietileno/nanofibras de polianilina e grafitept_BR
dc.typedoctoralThesispt_BR
dc.degree.grantorPontifícia Universidade Católica do Rio Grande do Sulpt_BR
dc.degree.departmentFaculdade de Engenhariapt_BR
dc.degree.programPrograma de Pós-Graduação em Engenharia e Tecnologia de Materiaispt_BR
dc.degree.levelDoutoradopt_BR
dc.degree.date2015pt_BR
dc.publisher.placePorto Alegrept_BR
Aparece en las colecciones:Dissertação e Tese

Ficheros en este ítem:
Fichero Descripción TamañoFormato 
000470698-Texto+Completo-0.pdfTexto Completo3,14 MBAdobe PDFAbrir
Ver


Todos los ítems en el Repositorio de la PUCRS están protegidos por derechos de autor, con todos los derechos reservados, y están bajo una licencia de Creative Commons Reconocimiento-NoComercial 4.0 Internacional. Sepa más.