dc.description.abstract | Um satisfatório grau de conversão do monômero é importante para melhorar a biocompatibilidade das resinas compostas. O objetivo deste estudo foi avaliar o efeito dos métodos de polimerização adicional na citotoxicidade de diferentes compósitos restauradores. Para isso foram confeccionadas 18 amostras de cada uma das seguintes resinas testadas: Filtek Z350XT® (3M/ESPE, St Paul, MN, EUA), Sinfony (3M/ESPE, St Paul, MN, EUA), Lava Ultimate (3M/ESPE, St Paul, MN, EUA). A cor usada em todas as reinas foi a A2 de corpo. Para as resinas Filtek Z350XT e Sinfony utilizaram-se moldes de politetrafluoretileno de 3x2mm. Para a resina Lava Ultimate foram cortados do bloco cubos com 1,6mm de face usando um disco diamantado e paquímetro digital. As amostras foram divididas em 4 grupos: Grupo FK: Filtek Z350XT polimerizada por 20s com LED, Grupo S: Sinfony com polimerização adicional com luz e vácuo, Grupo L: Lava Ultimate, Grupo FPA: Filtek Z350XT com polimerização adicional com luz e vácuo. As espécies avaliadas estiveram em contato com meio DMEM por um período de incubação de 24, 48 e 72 horas respectivamente. Após, o meio de cultura foi colocado em contato com as células de fibroblastos NIH/3T3. Teste de MTT foi realizado para análise da viabilidade celular. Testes de Levene e Kolmogorov-Smirnov (α=0,05) foram utilizados para análise estatística. O grupo S apresentou-se com a citotoxicidade mais baixa. Já a polimerização adicional no grupo FK não mostrou-se eficiente para a viabilidade celular. A resina Sinfony apresentou a menor citotoxicidade dentre os três materiais analisados. Uma polimerização adicional por luz e vácuo na resina Filtek Z350XT não melhora seu resultado para citotoxicidade quando comparado a polimerização direta da mesma. | pt_BR |
dc.description.abstract | An appropriate monomer conversion of composite resins is very important to improve your biocompatibility. The aim of this study was to evaluate additional polymerization methods of dental resins cytotoxicity. A total of 72 samples were prepared from the following materials: Filtek Z350XT® (3M/ESPE, St Paul, MN, EUA), Sinfony (3M/ESPE, St Paul, MN, EUA), Lava Ultimate (3M/ESPE, St Paul, MN, EUA). The used color was A2 for all composite resins. To Filtek Z350XT and Sinfony a Teflon mould (3x2mm) was used. From Lava Ultimate block 1,6mm cubes was cutting with diamond discs and digital pachymeter. Samples was divided in 4 groups: FK Group: 20s LED polymerization, S Group: Sinfony with light and vacuum additional polymerization, L Group: Lava Ultimate, FPA Group: Filtek Z350XT with light and vacuum additional polymerization. Evaluate specimens was stored in DMEM medium for 24, 48 and 72 hours respectively. Thereafter, culture medium was in contact with NIH/3T3 fibroblasts. MTT test determined cellular viability. Statistical analysis realized by Levene and Kolmogorov-Smirnov tests (α=0,05). The S group show the lower cytotoxicity. Additional polymerization of FK group wasn´t efficient to cellular viability. Sinfony presented minor cytotoxicity among all tested materials. Light and vacuum additional polymerization of Filtek Z350XT don´t improve your cytotoxicity results when compared with direct polymerization of the same dental composite. | en_US |
dc.language.iso | Português | pt_BR |
dc.publisher | Pontifícia Universidade Católica do Rio Grande do Sul | pt_BR |
dc.rights | openAccess | en_US |
dc.subject | ODONTOLOGIA | pt_BR |
dc.subject | MATERIAIS DENTÁRIOS | pt_BR |
dc.subject | RESINAS COMPOSTAS | pt_BR |
dc.subject | POLIMERIZAÇÃO | pt_BR |
dc.title | Análise da citotoxicidade de compósitos restauradores para técnica direta e indireta: estudo in vitro | pt_BR |
dc.type | masterThesis | pt_BR |
dc.degree.grantor | Pontifícia Universidade Católica do Rio Grande do Sul | pt_BR |
dc.degree.department | Faculdade de Odontologia | pt_BR |
dc.degree.program | Programa de Pós-Graduação em Odontologia | pt_BR |
dc.degree.level | Mestrado | pt_BR |
dc.degree.date | 2015 | pt_BR |
dc.publisher.place | Porto Alegre | pt_BR |
Aparece en las colecciones: | Dissertação e Tese
|