dc.contributor.advisorMenezes, Luciane Macedo de
dc.contributor.authorHenkin, Fernanda de Souza
dc.date.accessioned2017-11-02T11:01:20Z-
dc.date.available2017-11-02T11:01:20Z-
dc.date.issued2017pt_BR
dc.identifier.urihttp://hdl.handle.net/10923/10850-
dc.description.abstractIntrodução: Durante o tratamento ortodôntico, frequentemente são utilizados dispositivos e aparelhos auxiliares que requerem soldagem para a sua confecção. Além do processo de soldagem convencional à prata, diferentes métodos – potencialmente mais biocompatíveis - podem ser utilizados. A resistência mecânica destas soldas é fundamental para seu sucesso e deve ser avaliada. Objetivo: Revisar os métodos de soldagem disponíveis para uso em Ortodontia e avaliar a força de união das soldas à tração em soldas ponto, prata, laser e TIG. Materiais e Métodos: 40 segmentos de fio de aço inoxidável de 0,8mm (Morelli, Sorocaba/SP, Brasil) foram soldados entre si através das técnicas de soldagem elétrica, à prata, a laser e TIG, sendo realizadas 10 soldagens para cada técnica. Foi realizado ensaio de tração por meio de uma máquina de ensaios universal (Emic DL- 2000), utilizando célula de carga de 1000 N e velocidade de 10 mm/min. Resultados: O grupo de soldagem à prata apresentou a maior média de resistência à tração (532,1N), seguido pelos grupos laser (419,8N), ponto (301,1N) e TIG (216,3N) respectivamente. Houve diferença significativa entre os grupos, e partir do teste post-hoc de Dunn identificou-se que esta diferença ocorreu entre os grupos laser e ponto (p=0,046), laser e TIG (p=0,016), ponto e prata (p=2,5e-05) e prata e tig (p=4,6e-06). Conclusões: A força de união de soldagens a laser pode ser comparável com à de soldagens à prata e apresenta-se como boa alternativa para uso em Ortodontia. As técnicas de soldagem a ponto e a TIG apresentaram força de união comparáveis e significativamente inferiores aos das soldagens a laser e à prata.pt_BR
dc.description.abstractIntroduction: During orthodontic treatment, the use of appliances and devices that require welding procedures is often needed. Besides conventional silver soldering, different joining methods – with potentially higher biocompatibility – can be used. The mechanical strength of the welded areas is critical for their success, and must be evaluated. Objective: To review the joining methods for orthodontic purpose and evaluate the strength – by tensile strength measurements – of Silver Soldering, Spot, laser and TIG welding. Materials and Methods: 40 stainless steel wire segments with 0.8 mm diameter (Morelli, Sorocaba/SP, Brasil) were joined by means of silver soldering, spot, laser and TIG welding. For each joining method, 10 specimens were produced. Tensile strength test was performed 24 hours after welding by means of a universal testing machine (Instron Corporation, Canton, USA) using a cell load of 1000 N with a crosshead speed of 10 mm/minute. Results: The highest tensile strenght mean values was obtained by silver soldering (532.1N), followed by laser (419.8N), spot (301.1N) and TIG (216,3N) welding. Statistically significant diferences were observed between the groups, and the Dunn post-hoc test revealed difference between laser and spot welding (p=0046), laser and tig (p=0.016), spot and silver (p=2.5e-05) and silver and TIG (p=4.6e-06). Conclusions: The strenght of the laser joints are comparable to the Silver soldering joints, and represent a favorable alternative for orthodontic use. The spot and TIG welding methods presented comparable and significantly lower strenghts in relation do laser and silver soldering methods.en_US
dc.language.isoPortuguêspt_BR
dc.publisherPontifícia Universidade Católica do Rio Grande do Sulpt_BR
dc.rightsopenAccessen_US
dc.subjectSOLDAGEMpt_BR
dc.subjectORTODONTIApt_BR
dc.subjectODONTOLOGIApt_BR
dc.titleAvaliação da força de união de diferentes técnicas de soldagem para uso em ortodontiapt_BR
dc.typemasterThesispt_BR
dc.degree.grantorPontifícia Universidade Católica do Rio Grande do Sulpt_BR
dc.degree.departmentFaculdade de Odontologiapt_BR
dc.degree.programPrograma de Pós-Graduação em Odontologiapt_BR
dc.degree.levelMestradopt_BR
dc.degree.date2017pt_BR
dc.publisher.placePorto Alegrept_BR
Aparece en las colecciones:Dissertação e Tese

Ficheros en este ítem:
Fichero Descripción TamañoFormato 
000484930-Texto+Parcial-0.pdfTexto Parcial150,06 kBAdobe PDFAbrir
Ver


Todos los ítems en el Repositorio de la PUCRS están protegidos por derechos de autor, con todos los derechos reservados, y están bajo una licencia de Creative Commons Reconocimiento-NoComercial 4.0 Internacional. Sepa más.